Send inquiry
Applications : can be use as seals or splices fissures and cracks from any building , such as ( a water works , swimming pool , impounding reservoir , power station , a dam , sewage treatment project , the system of water supply and drainage , etc .
Feature : neutral , non-poisonous , non-pollution , great mechanical property , weather fastness , high and low pressure resistant, long service life, and it has excellent antiseep adhesive property .
Color: black , white , gray , and other colors which customer needs .
Packaging details: part A ,200L/Bucket (Net content 180L) , part B ,300ml , 500ml/piece
Storage condition: Airtight store in a cool ventilated dry place , under normal temperature . Storage life is 12 months from date of manufacture .
Announcements: must keep the building drying, cleaning and no-oil before use it (could use blast burner or hot-air blower to make drying ) , the material surface temperature should be 15ºC-27ºC when you use it , it can not be use if the material surface temperature is under 4ºC or exceed 40ºC , and it can not be uses on frosty or moist surface .
Performance Parameter:
Feature : neutral , non-poisonous , non-pollution , great mechanical property , weather fastness , high and low pressure resistant, long service life, and it has excellent antiseep adhesive property .
Color: black , white , gray , and other colors which customer needs .
Packaging details: part A ,200L/Bucket (Net content 180L) , part B ,300ml , 500ml/piece
Storage condition: Airtight store in a cool ventilated dry place , under normal temperature . Storage life is 12 months from date of manufacture .
Announcements: must keep the building drying, cleaning and no-oil before use it (could use blast burner or hot-air blower to make drying ) , the material surface temperature should be 15ºC-27ºC when you use it , it can not be use if the material surface temperature is under 4ºC or exceed 40ºC , and it can not be uses on frosty or moist surface .
Performance Parameter:
| Project | Index | Result | Test method | ||||
| 1 | Surface drying time , h | ≤1.5 | 1.0 | GB/T 13477.5 |
|||
| 2 | Sag , mm | Vertical , mm | ≤3 | 0 | |||
| Horizontal | Unchanged | Unchanged | |||||
| 3 | Elastic recovery , % | ≥60 | 69 | ||||
| 4 | Tensile adhesion |
Tensile strength , MPa | 23ºC | ≥0.4 | 0.35 | ||
| -20ºC | ≥0.6 | 0.50 | |||||
| Elongation at break , % | ≥200 | 385 | |||||
| 5 | Tensile properties at maintained extension , % | Non- damaging | Non- damaging | ||||
| 6 | Tensile properties at maintained extension after ultraviolet aging | Non- damaging | Non- damaging | ||||
| 7 | Tensile properties at maintained extension after immersion in water | Non- damaging | Non- damaging | ||||
| 8 | Pollution | Depth of pollution | ≤2.0 | 0 | GB/T23261 | ||
| Breadth of pollution | ≤2.0 | 0 | |||||